Hard Herbal Foam

This podiatric material stands out for its lightweight, ease of polishing, and dynamic adaptability. Its closed-cell structure and thermoconformable nature allow for a progressive adaptation to the anatomy of the foot, aiding in a better distribution of loads. It is especially indicated for the top part of insoles, also acting as an ideal stabilizer for stabilizations and postings. This material can be combined with itself or with other materials for a personalized and optimal fit.

This dark brown or black material, very lightweight, easy to polish, and with closed cells, is ideal for the manufacture of podiatric insoles. Its dynamic adaptability and stabilizing function make it perfect for various podiatric applications, providing consistent and lightweight insoles.

USAGE INDICATIONS:

• Manufacture of podiatric insoles.
• Cushioning and shock absorption.
• Stabilization and posting.

TECHNICAL CHARACTERISTICS:

Material: Chemically cross-linked polyethylene foam.

Composition: Chemically cross-linked polyethylene foam.

Color: Dark brown or black.

Thickness: 5.0 mm, 7.0 mm, 10.0 mm.

Measurements:

• 120 x 100 cm.
• 110 x 100 cm.
• 105 x 100 cm.

Hardness: Shore A: 65° (Medium).

Thermoformable: Yes.

Thermoforming Temperature: 70 to 90°C maximum

Instructions for Use:

• Mold the material at the specified temperature to adapt it to the desired shape.
• Use in the manufacture of insoles, ensuring a precise and comfortable fit.

Storage:

• Store in a cool, dry place.
• Protect from direct sunlight.

References and Dimensions:

• 11.107.8: Black, 120 x 100 cm, 5.0 mm
• 11.107.11: Dark brown, 120 x 100 cm, 5.0 mm
• 11.107.12: Dark brown, 110 x 100 cm, 10.0 mm
• 11.107.17: Dark brown, 105 x 100 cm, 7.0 mm